High Compressibility Iron Powder

Original
price: Negotiable
minimum:
Total supply:
Delivery term: The date of payment from buyers deliver within days
seat: Shanghai
Validity to: Long-term effective
Last update: 2019-11-22 16:56
Browse the number: 226
inquiry
Company Profile
 
 
Product details

LAP100.29H is a type of ultra-pure water atomised iron powder, with AD 2.95-3.10g/cm3, with good compression performance, and is widely used in high strength, high density sintered structural PM parts.

·High purity, easy compression, good fluidity, used for the production of high density PM structural parts.

·Fixed-volume batch mixing, maintaining the stability of different batches of powder.

·Irregular particle shape, compactibility.

·High purity, used as the iron magnetic material base.


Product standard and content(wt%)

Composition

Fe

C

S

Si

Mn

P

O

Al

Cr

Ti

V

Cu

Ni

Standard

≥99.5

≤0.01

≤0.012

≤0.04

≤0.12

≤0.012

≤0.12

-

-

-

-

-

-

Classic

99.65

0.003

0.008

0.02

0.08

0.01

0.08

0.005

0.01

0.001

0.006

0.02

0.007


Sieve analysis (particle size distribution)

μm

180

180/150

150/106

106/75

75/45

-45

wt%

0

≤10

balance

balance

balance

15-30

Classic

0

2

20.2

24.7

31.5

21.6





Properties

Under sintering temperature of 1120℃, sintering hardness (HRB)90; Tensile strength(MPa) 485; Elongation(%)1.75; Impact powder(J)18.5; Sintering expansion rate 0.25%.


Package and delivery

1000kg per big flexbag and 25kg per small bag packed into one big bag




Application

This type of metal powder can be used for the material of powder metallurgy sinter component parts.

LAP100.29H is widely used for the production of sintered metal parts with density above 6.8g/cm3 and PM forged parts.